Flowable Restorative Material - NEW Economy kit - 4x1gr syringes (A1, A2, A3 & A3.5) COMPARES TO: Revolution by Kerr™ Flow is a visible-light activated, radiopaque, flowable composite. 
The excellent flowable consistency characteristics makes ProFil™ Flow an ideal composite for filling cavities. ProFil™ Flow is available in more than 4 shades.

Features
• Excellent esthetic properties 
• No oozing or slumping 
• Perfect for minimal invasive restorations 
• Low Viscosity 
• Maximum versatility 
• High polish retention & stable color match 
• Long term fluoride release 
• Low shrinkage 
• Indications 
• Class III, Class V, Smaller Class IV restorations 
• Base/liner in Class I & Class II restorations 
• Repair of resin, porcelain and acrylic temporary materials 
• Pit & Fissure sealant 
• Restoration of minimally invasive cavity preparations 
• Undercut blockout

Physical Properties 
ProFil™, a micro hybrid composite has outstanding physical properties that provide excellent wear resistance. 
Sensitivity to ambient light Above 100 sec. 
Weight of total inorganic filler 78% 
Volume of total inorganic filler 59% 
Depth of cure > 1.5 mm 
Compressive strength > 230 MPa 
Flexural Strength > 120MPa 
Water Absorption < 40 µg / Щ 
Solubility < 7.5 µg / Щ

$74.00 $104.00
$74.00 $104.00

Dispersed Phase Alloy 69.5%Ag, High Copper, Non Gamma II.
Nogama® is an admix of spherical, copper-silver eutectic particles and lathe–cut conventional alloy. 
Nogama® provides a firm pack and smooth carving.

• Special controlled compositions are available and developed according to design procedures in compliance to ISO 13485:2012


Features
• Increased strength of restored teeth
• Excellent durability
• Corrosion resistant
• Supreme marginal adaptability

Nogama® has a high compressive strength that minimizes the risk of restoration fracture. 
Composition Ag 69.5%, Sn 19.5%, Cu 10.5%, Zn 0.5%

• Particle Shape 80% Lathe cut 20% spherical
• Average Creep (7 days) 0.35%
• Average Dimensional Change +0.08%
• Average Compressive Strength (1hr) 164 MPa
• Average Compressive Strength (24hr) 470 MPa

Nogama® has excellent handling characteristics and makes it ideal for large restorations

Conforms to: 
ISO 24234
Mercury and Alloys for dental amalgam
Description: K-Files 31mm #40 6/Box. Stainless Steel.
Manufacturer Code: PKF3140
Brand: Pulpadent
Length: 31 mm
Material: Stainless steel
Packaging: Box of 6 files
Size: 40
$35.00 $59.00
$35.00 $59.00

Universal Dental Restorative Material - Advanced Nano Technology **Compare to TPH 3, Point 4, Herculite XRV, Filtek Z100 & Z250 

 *APRIL SPEICAL BUY 6 GET 2 FREE*


ProFil™, is a new micro hybrid composite material for use in both anterior and posterior restorations. 
ProFil™ composite resin is the perfect combination of simplicity and exceptional esthetics.

Features
• High polishability 
• Non sticky formula 
• Optimal balance of physical properties 
• Light cured, radiopaque & color stable 
• Low polymerization shrinkage 
• Fast placement technique, easy to apply & sculpt 
• High strength & wear resistance 
• Available in 14 shades

Physical Properties 
ProFil™, a micro hybrid composite has outstanding physical properties that provide excellent wear resistance. 
Sensitivity to ambient light Above 100 sec. 
Weight of total inorganic filler 78% 
Volume of total inorganic filler 59% 
Depth of cure > 1.5 mm 
Compressive strength > 230 MPa 
Flexural Strength > 120MPa 
Water Absorption < 40 µg / Щ 
Solubility < 7.5 µg / Щ

$79.00 $110.00
$79.00 $110.00

Dual Cure Bulk Fill Composite
ProFil™ BULK is a dual cure dental restorative composite designed for direct restorations. It is suitable for bulk fill
technique in the posterior region and can be applied in an unlimited layer thickness.

Features
• Unlimited depth of cure
• Dual curing mechanism
• Compatible with all methacrylate-based dental bonding agents
• Superior compressive strength
• Utilization of intercalated and exfoliated nano-composite technology
• Easy-to-use and apply using an industry standard, auto-mix dispensing system. Saves time and provides a
consistent, homogeneous mix

 

Compressive Strength 250 MPa
Linear Shrinkage 1.2%
Compatible with halogen light Yes
Compatible with Plasma ark light lamp Yes
Compatible with LED Yes
Depth of Cure Irradiation by LED – for 20 sec. 8.0 mm
Depth of Cure Irradiation by Halogen light – for 20 sec 8.0 mm
Working Time 1.5 - 3.5 min
Setting Time 2.5 - 4.5 min
Average Filler Concentration (by weight) 60 wt%
Shelf Life 2 Years

$79.00 $110.00
$79.00 $110.00

Light-Cure Self Adhesive Flowable Composite
ProFil™ Flow SE is a light cure self-etching, self-adhesive, radiopaque, flowable composite. Combining  3 in one ProFil Flow SE features the  benefits of adhesive and restorative technology thus simplifying direct restorative procedures. With this flowable dental composite there is no need to bond separately, reducing steps and saving time.
ProFil Flow SE is faster, easier, safer and is the ideal restorative material for pediatric patients.

Features
• Ready for use
• Etching, bonding and filling in one step
• Does not open dentin tubules
• Radiopaque
• Esthetic
• Increases profitability
• Ideal for pediatric patients

 

Properties
Inorganic filler particle size (d50 - d50)
0.02 - 2.3μm
Volume of inorganic fillers ca.
43%-vol.
Working time (full operating light)
≥01:00 min.
Recommended thickness of layers
≤ 2 mm
Recommended curing time (LED-/ Halogen lamp)
≥ 20 sec.
Depth of cure (20s curing time)
≥ 2 mm
Flexural strength ( = transverse strength)
≥ 90 MPa
Radiopacity
≥160% Al
Adhesion to enamel
≥ 3 MPa
Compressive strength
≥ 260 MPa
Water solubility
≤3 μg/mm3
Flexural modulus (= transverse modulus)
≥ 4 GPa
$90.00 $120.00
$90.00 $120.00

Resin Reinforced Glass Ionomer cement
ProGlass Plus™, a resin modified glass ionomer luting cement, bonds chemically and mechanically to tooth structure and to all types of core material. 
ProGlass Plus™ is designed for final cementation of metal, porcelain-fused-to-metal and metal free crowns, bridges, inlays and onlays.

Features
• Higher bond strengths than conventional glass ionomer cements 
• Simple placement technique 
• Low coefficient of thermal expansion 
• Maintains all benefits of true glass Ionomer 
• Excellent biocompatibility to tooth structure and soft tissues. 
• Fluoride release

 

Physical Properties 
• Cementation of all types of metal, porcelain fused to metal, resin crowns, inlays, onlays and bridges 
• Cementation of porcelain inlays 
• Cementation to all types of core material including prefabricated pins , posts and cast posts 
• Cementable reinforced all ceramic crowns

Powder/Liquid Working Kit (15g/6.8ml) 
Trial Size Powder/Liquid Kit (8g/5ml) 
Coming Soon - Innovative GI Capsule (Box of 50)

$129.00 $230.00
$129.00 $230.00

Light Cure, Glass Ionomer Liner/Base
ProBase™ is a reinforced glass-ionomer cement that is designed for use as a luting/lining cement. 
ProBase™ is the perfect liner/base solution to help protect dentin.

Features
• Flouride release 
• Light cure command set 
• Strong adhesion to dentin 
• Excellent radiopacity 
• Good biocompatibility 
• Excellent mechanical properties

 

Liner/Base underneath composites, amalgam, ceramic & metal restorations

Physical Properties
 
Based on its excellent adhesion qualities, ProBase™ can be used under any kind of restorative material. 
ProBase™ exhibits high radiopacity, high strength and snap set. 

• Recommended setting time 20sec 
• Depth of cure > 4mm 
• Compression strength > 110 MPa 
• Diametral Tensile Strength > 20 MPa 
• Flexural Strength 44 MPa 
• Adhesion to conditioned dentin > 8MPa

Coming Soon! New Innovative Luer Lock GI Capsule (box of 50)

$110.00 $150.00
$110.00 $150.00

ProGlass™ Silver - Silver Reinforced Glass Ionomer Cement
ProGlass™ Silver is a mercury free fluoride releasing silver restorative. Designed to offer strong abrasion resistance, ProGlass™ Silver offers a unique blend of spherical silver-tin alloy with glass ionomer, providing an ultimate balance between working and setting time. ProGlass™ Silver is ideal for lasting core build-ups, block-outs and repair and can also be used in cases where radiopacity is required.

Features
• Unique blend of 100% spherical silver-tin alloy with glass ionomer 
• Versatile clinical application 
• Strong abrasion resistant 
• Optimal level of radiopacity 
• Fluoride Release

Physical Properties 
• Core build-up 
• Restoration of primary teeth 
• Base or liner 
• Class I, limited Class II, temporary fillings

Powder/Liquid Working Kit (20g/10ml) 
Trial Size Powder/Liquid Kit (8g/5ml)) 

Conforms to: 
ISO 9917:2003

$60.00 $90.00
$60.00 $90.00
Glass Ionomer Luting Cement
ProGlass™ One chemically bonds to tooth structure & metal providing excellent strength and marginal integrity for long term restorations. 
ProGlass™ One is designed for final cementation of metal inlays, onlays, posts and orthodontic brackets

Features
• Excellent marginal seal 
• Minimizes microleakage 
• Easy seating of restoration 
• Superior longevity and restoration integrity 
• No need for primer or adhesive 
• Fluoride release 
• Enhanced physical properties